TY  - GEN
A1  - Picht, Oliver
Y1  - 2010///
KW  - bismuth telluride 
KW  -  thermoelectric material 
KW  -  nanowire 
KW  -  electrodeposition 
KW  -  ion track-etched membrane
UR  - https://archiv.ub.uni-heidelberg.de/volltextserver/10721/
N2  - Polycrystalline Bi2Te3 nanowires are electrochemically grown in ion track-etched polycarbonate membranes. Potentiostatic growth is demonstrated in templates of various thicknesses ranging from 10 to 100 µm. The smallest observed nanowire diameters are 20 nm in thin membranes and approx. 140 -180 nm in thicker membranes. The influence of the various deposition parameters on the nanowire growth rate is presented. Slower growth rates are attained by selective change of deposition potentials and lower temperatures. Nanowires synthesized at slower growth rates have shown to possess a higher degree of crystalline order and smoother surface contours. With respect to structural properties, X-ray diffraction and transmission electron microscopy verified the growth of Bi2Te3 and evidenced the stability of specific properties, e.g. grain size or preferential orientation, with regard to variations in the deposition conditions. The interdependency of the fabrication parameters, i.e. temperature, deposition potential and nanochannel diameters, is demonstrated for wires grown in 30 µm thick membranes. It is visible from diffraction analysis that texture is tunable by the growth conditions but depends also on the size of the nanochannels in the template. Both (015) and (110) reflexes are observed for the nanowire arrays. Energy dispersive X-ray analysis further points out that variation of nanochannel size could lead to a change in elemental composition of the nanowires.
TI  - Growth and Characterization of Bismuth Telluride Nanowires
ID  - heidok10721
AV  - public
ER  -